h13 skd61 1.2344 steel sheet

h13 skd61 1.2344 steel sheet 1.wide used in die manufacturing. 2.High hardenability steel. 3.High tougness. 4.Large stocks

Hot work mould steel sheet 1.2344, alloy steel sheet 1.2344/H13/ SKD61/ 4Cr5MoSiV1

1.Specifications

1)Round bar:Diameter : 1mm-2000mm

2)Square bar:Size:  50mm * 50mm-600mm *600mm

3)Plate steel/flat bar:Size: Thickness:  0.1mm-800mm Width: 10mm to 1500mm

4)Steel sheet: .

Cold-rolled sheet: Thickness:  2-5mm Width:1000mm Length: 2000mm

Hot-rolled sheet: Thickness:6-80mm Width: 210-610mm

Length:  We can supply any length based on the customer's requirement.

2.Chemical composition(for reference only)

Steel	C	Si	Mn	P	S	Cr	Mo	V	HBW
4Cr5MoSiV1	0.32-0.42	0.80-1.20	0.20-0.50	≤0.030	≤0.030	4.75-5.50	1.10-1.75	0.80-1.20	≤235
1.2344	0.35-0.42	0.80-1.20	0.25-0.50	≤0.030	≤0.020	4.80-5.50	1.20-1.50	0.85-1.15	≤229
H13	0.32-0.45	0.80-1.20	0.20-0.50	≤0.030	≤0.030	4.75-5.50	1.10-1.75	0.80-1.20	≤235

3.Delivery condition of 1.2344 alloy steel: 

1)Trade patters: CIF or FOB

   2).Packed: According to the customer's request

   3) Payment: L/C or T/T

   4) Some stock available. 

   5) Annealed Hardness : HRC<24 

   6) EAF or ESR, Hot rolled or forged Peeled or black surface, annealed or QT. 

4.Heat treatment of  1.2344 alloy steel: :

Annealing	750 °C ~800 °C
Hardness after annealing	Max :HB<205
Stress relieving	600°C ~650 °C
Hot forming	900°C ~1100 °C
Hardening	1020°C ~1080 °C
Quenching media	Oil, Salt bath ( 500°C ~ 550 °C ), Air
Hardness after quenching	HRC 52 °C ~ 56°C Oil, Salt bath; 50 - 54 HRC Air

5.Hardness after tempering:

Tempering °C	400	500	550	600
HRC	54	55	54	50

 6.Characteristic of 1.2344 alloy steel: 

 1)high hardenability, high toughness, good ductility, high temperature performance

   the use of Electric arc furnace(EBT)+refining(lf)+Vacuum(CD) make the production of die steel are in high purity and   good performance

2)high hot strength and hardness

   good resistence to heat, good hot toughness, high resistance to temperature fatigue and

wear in medium heat small heat deformation

 the tendency of the appearing of iron oxide skin are small in air-quenching

    excellent corrosion resistance

3)Hot-work steel with good high temperature strength and high wear resistance.

7.Application of 1.2344 steel:

    Highly stressed hot work tools and dies, pressure casting dies for light metals, mandrels, dies, liners, dieholders, bolsters, stems, punches, dummy blocks and containers for metal tube and rod extrusion tools, hot shear blades, hot forming and forging dies for steels, brass and aluminum, tools and dies for the manufacture of hollow bodies, screws,nuts, rivets and bolts, moulds, worms and cylinders for the processing of plastics, press dies and die inserts, rolls for profiling tools,hot extrusion equipments, trimming tools, plastic moulding dies, severe cold punching, scrap shears, shrink rings, wear

 resisting parts, cold heading die casings, hot gripper and header dies, nitrided ejectors.

Chinese	American	German	Swedish	Japanese
GB	AISI	DIN	ASSAB	JIS
4Cr5MoSiV1	H13	1.2344	8407	SKD61

 

8.Heat treatment (for reference)

Quenching centigrade degree	Tempering centigrade degree/ HRC
1010~1060 centigrade degree	100	200	300	400	500	550	600	650	700
Air,oil or salt bath	52	52	52	54	54	54	50	42	32

 

h13 skd61 1.2344 steel sheet